Packing Pillar #6711 Non-asbestos Braided

810581 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 3MMX3MTR

IMPA:810581

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810582 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 5MMX3MTR

IMPA:810582

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810583 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 6.5MMX3MTR

IMPA:810583

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810584 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 8MMX3MTR

IMPA:810584

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810585 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 9.5MMX3MTR

IMPA:810585

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810586 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 11MMX3MTR

IMPA:810586

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810587 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 12.5MMX3MTR

IMPA:810587

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810588 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 14.5MMX3MTR

IMPA:810588

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810589 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 16MMX3MTR

IMPA:810589

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)

810591 PACKING NON ASBESTOS HI-TEMP, HI-PRESSURE #6711 19MMX3MTR

IMPA:810591

MTML UOM:BX

Pillar No. 6711 Structure: A graphite packing made of braided expanded graphite yarn reinforced with NCF600 wire with its surface being coated with graphite powder. Features: Can be used without top and bottom adaptor packing. Application: It is suitable for high-temperature and high pressure valves. Performance: Temperature -200 to 600oC (at oxygen atmosphere limited to 450oC), Pressure to 25.9 MPaG (264 kgf/cm2) (Class 1500)